%0 Journal Article
%A Grushko, Benjamin
%A Kapush, Denys
%A Samuha, S.
%A Meshi, L.
%T A study of the Al-Pd-Pt alloy system
%J Journal of alloys and compounds
%V 600
%@ 0925-8388
%C Lausanne
%I Elsevier
%M FZJ-2014-06422
%P 125 - 129
%D 2014
%X The constitution of the Al−Pd−Pt alloy system was studied above 35 at.% Al at 700, 780, 900 and 1100 °C. The experiments revealed the formation of wide extensions of the binary Al−Pd and Al−Pt phases but no ternary phases. Continuous regions are probably formed between the isostructural phases Al4TM, Al21TM8, high-temperature AlTM, low-temperature AlTM and Al3TM5 (TM = Pd or Pt). The continuity between the Al3TM2 phases was revealed at 900 °C, while at 1100 °C the regions mutually extended from Al3Ni2 and Al3Pd2 are separated by the ternary extension of Al2Pt. The latter phase was found to dissolve up to 24 at.% Pd, which resulted in a sharp decrease of its Al concentration. The Al−Pd ε-phase was found to extend up to 18 at.% Pt at practically constant Al, while the Al−Pt ξ-phase was found to extend up to 7 at.% Pd.
%F PUB:(DE-HGF)16
%9 Journal Article
%U <Go to ISI:>//WOS:000333766500021
%R 10.1016/j.jallcom.2014.02.109
%U https://juser.fz-juelich.de/record/173008