TI  - A study of the Al-Pd-Pt alloy system
JO  - Journal of alloys and compounds
VL  - 600
SN  - 0925-8388
CY  - Lausanne
PB  - Elsevier
M1  - FZJ-2014-06422
SP  - 125 - 129
PY  - 2014
AB  - The constitution of the Al−Pd−Pt alloy system was studied above 35 at.% Al at 700, 780, 900 and 1100 °C. The experiments revealed the formation of wide extensions of the binary Al−Pd and Al−Pt phases but no ternary phases. Continuous regions are probably formed between the isostructural phases Al4TM, Al21TM8, high-temperature AlTM, low-temperature AlTM and Al3TM5 (TM = Pd or Pt). The continuity between the Al3TM2 phases was revealed at 900 °C, while at 1100 °C the regions mutually extended from Al3Ni2 and Al3Pd2 are separated by the ternary extension of Al2Pt. The latter phase was found to dissolve up to 24 at.% Pd, which resulted in a sharp decrease of its Al concentration. The Al−Pd ε-phase was found to extend up to 18 at.% Pt at practically constant Al, while the Al−Pt ξ-phase was found to extend up to 7 at.% Pd.
LB  - PUB:(DE-HGF)16
UR  - <Go to ISI:>//WOS:000333766500021
DO  - DOI:10.1016/j.jallcom.2014.02.109
UR  - https://juser.fz-juelich.de/record/173008
ER  -