@ARTICLE{Grushko:173008,
      author       = {Grushko, Benjamin and Kapush, Denys and Samuha, S. and
                      Meshi, L.},
      title        = {{A} study of the {A}l-{P}d-{P}t alloy system},
      journal      = {Journal of alloys and compounds},
      volume       = {600},
      issn         = {0925-8388},
      address      = {Lausanne},
      publisher    = {Elsevier},
      reportid     = {FZJ-2014-06422},
      pages        = {125 - 129},
      year         = {2014},
      abstract     = {The constitution of the Al−Pd−Pt alloy system was
                      studied above 35 $at.\%$ Al at 700, 780, 900 and 1100 °C.
                      The experiments revealed the formation of wide extensions of
                      the binary Al−Pd and Al−Pt phases but no ternary phases.
                      Continuous regions are probably formed between the
                      isostructural phases Al4TM, Al21TM8, high-temperature AlTM,
                      low-temperature AlTM and Al3TM5 (TM = Pd or Pt). The
                      continuity between the Al3TM2 phases was revealed at 900
                      °C, while at 1100 °C the regions mutually extended from
                      Al3Ni2 and Al3Pd2 are separated by the ternary extension of
                      Al2Pt. The latter phase was found to dissolve up to 24
                      $at.\%$ Pd, which resulted in a sharp decrease of its Al
                      concentration. The Al−Pd ε-phase was found to extend up
                      to 18 $at.\%$ Pt at practically constant Al, while the
                      Al−Pt ξ-phase was found to extend up to 7 $at.\%$ Pd.},
      cin          = {PGI-5},
      ddc          = {670},
      cid          = {I:(DE-Juel1)PGI-5-20110106},
      pnm          = {424 - Exploratory materials and phenomena (POF2-424)},
      pid          = {G:(DE-HGF)POF2-424},
      typ          = {PUB:(DE-HGF)16},
      UT           = {WOS:000333766500021},
      doi          = {10.1016/j.jallcom.2014.02.109},
      url          = {https://juser.fz-juelich.de/record/173008},
}