%T THE Al-Cr-Fe PHASE DIAGRAM. I. PHASE EQUILIBRIA AT SUBSOLIDUS TEMPERATURES OVER COMPOSITION RANGE 58-100 AT.% Al
%J Powder metallurgy and metal ceramics
%V 50
%@ 1068-1302
%C Dordrecht [u.a.]
%I Springer Science + Business Media B.V
%M PreJuSER-19367
%P 83 - 97
%D 2011
%Z Record converted from VDB: 12.11.2012
%X Based on transmission and scanning electron microscopy, x-ray diffraction, electron microprobe and differential thermal analyses, the solidus surface of the ternary Al-Cr-Fe system is constructed for the first time on the concentration triangle over composition range 58-100 at.% Al. Four ternary compounds, D-3, O-1, H, and epsilon, with decagonal, orthorhombic base-centered, hexagonal, and orthorhombic primitive lattices participate in phase equilibria on the solidus surface. Solid solutions based on aluminum and binary compounds as well as ternary phases form 12 single-phase surfaces, 25 ruled surfaces of two-phase equilibria bounding two-phase regions, and 14 three-phase isothermal planes corresponding to invariant four-phase equilibria on the solidus surface.
%K J (WoSType)
%F PUB:(DE-HGF)16
%9 Journal Article
%U <Go to ISI:>//WOS:000292308700009
%U https://juser.fz-juelich.de/record/19367