TY  - JOUR
AU  - Kordoš, P.
AU  - Mikulics, M.
AU  - Stoklas, R.
AU  - Čičo, K.
AU  - Dadgar, A.
AU  - Grűtzmacher, D.
AU  - Krost, A.
TI  - Thermally Oxidized InAlN of Different Compositions for InAlN/GaN Heterostructure Field-Effect Transistors
JO  - Journal of electronic materials
VL  - 41
IS  - 11
SN  - 1543-186X
CY  - Warrendale, Pa
PB  - TMS
M1  - FZJ-2015-05154
SP  - 3013 - 3016
PY  - 2012
AB  - Properties of InAlN/GaN heterostructure field-effect transistors with thermally oxidized (750°C, 2 min) InAlN barrier layers of different compositions (InN = 13%, 17%, and 21%) were evaluated. The saturation drain current was inversely proportional to the InN content and was lower than that obtained with nonoxidized devices. From the capacitance measurement, the resulting sheet charge density decreased from 1.1 × 1013 cm−2 to 0.6 × 1013 cm−2 with increased InN content, and it was only approximately 50% of that of the nonoxidized counterparts. The oxide thickness of approximately 1 nm was extracted from the zero-bias capacitances. The pulsed measurements yielded a very high gate lag independent from the InAlN composition (the pulsed-to-static drain current ratio was ∼0.5 for a 200-ns pulse width). On the other hand, a significantly lower gate lag was observed on nonoxidized SiN x passivated InAlN/GaN devices. The results demonstrate that a high density of trap states was created in the thermally oxidized InAlN/GaN structures.
LB  - PUB:(DE-HGF)16
UR  - <Go to ISI:>//WOS:000309677200004
DO  - DOI:10.1007/s11664-012-2096-4
UR  - https://juser.fz-juelich.de/record/203145
ER  -