000279585 245__ $$aEffect of In-Situ Gas Changes on ThermallyGrown Chromia Scales Formed on Ni-25Cr Alloy at 1000°C in Atmospheres With and Without Water Vapour
000279585 260__ $$aAmsterdam [u.a.]$$bElsevier Science$$c2015
000279585 3367_ $$0PUB:(DE-HGF)16$$2PUB:(DE-HGF)$$aJournal Article$$bjournal$$mjournal$$s1449824366_10435
000279585 3367_ $$2DataCite$$aOutput Types/Journal article
000279585 3367_ $$00$$2EndNote$$aJournal Article
000279585 3367_ $$2BibTeX$$aARTICLE
000279585 3367_ $$2ORCID$$aJOURNAL_ARTICLE
000279585 3367_ $$2DRIVER$$aarticle
000279585 520__ $$aRegarding oxidation resistance, most high temperature alloys rely on the formation of a protective chromia surface scale during service. In the present study, the oxidation behaviour of a Ni–25%Cr model alloy was investigated during single- and two-stage oxidation in Ar–O2 and Ar–H2O gas mixtures at 1000°C. In the two-stage experiments, the test gas was changed after a predefined oxidation time from dry to wet gas, and vice versa, without intermediate specimen cooling. Oxidation kinetics were measured using thermogravimetry and post exposure characterisation was accomplished using scanning and transmission electron microscopy, focused ion beam and energy dispersive X-ray spectroscopy techniques. The single stage exposure to Ar–O2 resulted in the formation of a voided, poorly adhering chromia scale exhibiting a coarse, equi-axed morphology. In Ar–7%H2O a fine, columnar grained oxide scale was formed which was free of microvoidage within the scale and at the scale/metal interface and therefore exhibited excellent adherence to the metallic substrate. During two-stage exposure to Ar–O2 and subsequently to Ar–H2O, a fine grained, columnar shaped oxide developed on top of the coarse oxide scale formed in the first oxidation stage. The opposite effect occurred when the exposure started in the wet environment. The mechanisms which are responsible for the observed oxidation features are discussed on the basis of classical oxidation theory in combination with previous results on oxidation of chromia forming alloys in oxygen rich gases and water vapour containing, low p(O2) environments.
000279585 536__ $$0G:(DE-HGF)POF3-111$$a111 - Efficient and Flexible Power Plants (POF3-111)$$cPOF3-111$$fPOF III$$x0
000279585 7001_ $$0P:(DE-HGF)0$$aGorr, B.$$b1
000279585 7001_ $$0P:(DE-Juel1)129729$$aHänsel, Michael$$b2
000279585 7001_ $$0P:(DE-Juel1)129794$$aShemet, Vladimir$$b3
000279585 7001_ $$0P:(DE-HGF)0$$aChrist, H. J.$$b4
000279585 7001_ $$0P:(DE-Juel1)129782$$aQuadakkers, Willem J.$$b5
000279585 773__ $$0PERI:(DE-600)2035150-1$$a10.1179/0960340914Z.000000000108$$n1-2$$p238-247$$tMaterials at high temperatures$$v32$$x0960-3409$$y2015
000279585 909CO $$ooai:juser.fz-juelich.de:279585$$pVDB
000279585 9101_ $$0I:(DE-588b)5008462-8$$6P:(DE-Juel1)129729$$aForschungszentrum Jülich GmbH$$b2$$kFZJ
000279585 9101_ $$0I:(DE-588b)5008462-8$$6P:(DE-Juel1)129794$$aForschungszentrum Jülich GmbH$$b3$$kFZJ
000279585 9101_ $$0I:(DE-588b)5008462-8$$6P:(DE-Juel1)129782$$aForschungszentrum Jülich GmbH$$b5$$kFZJ
000279585 9131_ $$0G:(DE-HGF)POF3-111$$1G:(DE-HGF)POF3-110$$2G:(DE-HGF)POF3-100$$3G:(DE-HGF)POF3$$4G:(DE-HGF)POF$$aDE-HGF$$bEnergie$$lEnergieeffizienz, Materialien und Ressourcen$$vEfficient and Flexible Power Plants$$x0
000279585 9141_ $$y2015
000279585 915__ $$0StatID:(DE-HGF)0100$$2StatID$$aJCR$$bMATER HIGH TEMP : 2014
000279585 915__ $$0StatID:(DE-HGF)0200$$2StatID$$aDBCoverage$$bSCOPUS
000279585 915__ $$0StatID:(DE-HGF)0199$$2StatID$$aDBCoverage$$bThomson Reuters Master Journal List
000279585 915__ $$0StatID:(DE-HGF)0111$$2StatID$$aWoS$$bScience Citation Index Expanded
000279585 915__ $$0StatID:(DE-HGF)0150$$2StatID$$aDBCoverage$$bWeb of Science Core Collection
000279585 915__ $$0StatID:(DE-HGF)1160$$2StatID$$aDBCoverage$$bCurrent Contents - Engineering, Computing and Technology
000279585 915__ $$0StatID:(DE-HGF)9900$$2StatID$$aIF < 5
000279585 9201_ $$0I:(DE-Juel1)IEK-2-20101013$$kIEK-2$$lWerkstoffstruktur und -eigenschaften$$x0
000279585 980__ $$ajournal
000279585 980__ $$aVDB
000279585 980__ $$aI:(DE-Juel1)IEK-2-20101013
000279585 980__ $$aUNRESTRICTED
000279585 981__ $$aI:(DE-Juel1)IMD-1-20101013