TI  - Hydrothermal degradation of cubic zirconia
JO  - Acta materialia
VL  - 51
SN  - 1359-6454
CY  - Amsterdam [u.a.]
PB  - Elsevier Science
M1  - PreJuSER-32009
SP  - 5123 - 5130
PY  - 2003
N1  - Record converted from VDB: 12.11.2012
AB  - Tetragonal ZrO2 undergoes a tetragonal to monoclinic transformation with the presence of water or water vapor when annealed at relatively low temperatures (65-400 degreesC); such a transformation has been shown to be due to the annihilation of oxygen vacancies. Nevertheless, cubic ZrO2 has always been presumed to be stable under similar conditions. However, after annealing at 250 degreesC under a vapor pressure of 2.6 x 10(-2) atm for 2 years, the 8 nmol% Y2O3-doped cubic ZrO2 ceramic samples cracked. Even though the sample phase was still predominantly cubic, subsequent X-ray diffraction studies indicated that a kind of phase transformation actually occurred, while TEM investigations and electron diffractions demonstrated the precipitation of monoclinic ZrO2. After annealing, the electrical conductivity of the sample was found to increase by about 30%, suggesting proton conduction. This is the first observation of the hydrothermal degradation in cubic ZrO2 (C) 2003 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.
KW  - J (WoSType)
LB  - PUB:(DE-HGF)16
UR  - <Go to ISI:>//WOS:000185811600016
DO  - DOI:10.1016/S1359-6454(03)00362-8
UR  - https://juser.fz-juelich.de/record/32009
ER  -