000045340 245__ $$aEffects of metallurgical chemistry and service conditions on the oxidation limited life time of FeCr-Al-based components
000045340 260__ $$aJülich$$bForschungszentrum Jülich GmbH Zentralbibliothek, Verlag$$c2002
000045340 3367_ $$0PUB:(DE-HGF)11$$2PUB:(DE-HGF)$$aDissertation / PhD Thesis
000045340 3367_ $$0PUB:(DE-HGF)3$$2PUB:(DE-HGF)$$aBook
000045340 3367_ $$02$$2EndNote$$aThesis
000045340 3367_ $$2DRIVER$$adoctoralThesis
000045340 3367_ $$2BibTeX$$aPHDTHESIS
000045340 3367_ $$2DataCite$$aOutput Types/Dissertation
000045340 3367_ $$2ORCID$$aDISSERTATION
000045340 4900_ $$0PERI:(DE-600)2414853-2$$82931$$aBerichte des Forschungszentrums Jülich$$v3948$$x0944-2952
000045340 502__ $$aAachen, Techn. Hochsch., Diss., 2002$$bDr. (FH)$$cTechn. Hochsch. Aachen$$d2002
000045340 500__ $$aRecord converted from VDB: 12.11.2012
000045340 520__ $$aFeCrAl alloys are high temperature structural materials with ever increasing technological importance, because in the temperature range of 900-1300°C their resistance against environmental attack exceeds that of other metallic materials . This is due to the formation of a protective alumina scale an the surface of FeCrAl-alloys during high temperature service. During exposure at elevated temperatures, the major life limiting factor for FeCrAl alloys is the depletion of the alloy Al-content. In the present work a number of commercial and model alloys have been studied with respect to the lifetime oxidation behaviour . The experimentally determined lifetimes were compared with those calculated based an the available lifetime prediction model. Analytical studies were performed an oxidised alloys using a range of surface analysis techniques to elucidate the oxidation mechanisms as a function of exposure time and temperature. The results demonstrate the importance of the minor alloying chemistry for scale growth rate and adherence and consequently for the service life of FeCrAl-based components . The observed differences in oxidation rates between the studied commercial materials and even between different batches of one commercial alloy have been found to originate from the interaction of typical minor alloying additions of the reactive elements, such as Y, La, Ti, Zr and Hf with typical alloy impurities of carbon and nitrogen. A major finding was that for this reason, the optimum oxidation resistance can not be achieved by one reactive element addition, but rather by a combination of the latter. The exact amounts, type and distribution of the reactive elements must be carefully selected depending an the particular alloy application .
000045340 536__ $$0G:(DE-Juel1)FUEK248$$2G:(DE-HGF)$$aWerkstoffsysteme für Kraftwerke$$cE03$$x0
000045340 655_7 $$aHochschulschrift$$xDissertation (FH)
000045340 7001_ $$0P:(DE-Juel1)129782$$aQuadakkers, Willem J.$$b1$$uFZJ
000045340 8564_ $$uhttps://juser.fz-juelich.de/record/45340/files/Juel_3948_Naumenko.pdf$$yOpenAccess
000045340 909CO $$ooai:juser.fz-juelich.de:45340$$pdnbdelivery$$pVDB$$pdriver$$popen_access$$popenaire
000045340 915__ $$0StatID:(DE-HGF)0510$$2StatID$$aOpenAccess
000045340 9141_ $$y2002
000045340 9131_ $$0G:(DE-Juel1)FUEK248$$bEnergie$$kE03$$lRationelle Energieumwandlung$$vWerkstoffsysteme für Kraftwerke$$x0
000045340 9201_ $$0I:(DE-Juel1)VDB2$$d31.12.2006$$gIWV$$kIWV-2$$lWerkstoffstruktur und Eigenschaften$$x0
000045340 970__ $$aVDB:(DE-Juel1)6873
000045340 9801_ $$aFullTexts
000045340 980__ $$aVDB
000045340 980__ $$aJUWEL
000045340 980__ $$aConvertedRecord
000045340 980__ $$aphd
000045340 980__ $$aI:(DE-Juel1)IEK-2-20101013
000045340 980__ $$aUNRESTRICTED
000045340 980__ $$aFullTexts
000045340 981__ $$aI:(DE-Juel1)IMD-1-20101013
000045340 981__ $$aI:(DE-Juel1)IEK-2-20101013