TY  - JOUR
AU  - Liang, T. X.
AU  - Zhao, H. S.
AU  - Tang, C. H.
AU  - Verfondern, K.
TI  - Irradiation performance and modeling of HTR-10 coated fuel particles
JO  - Nuclear engineering and design
VL  - 236
SN  - 0029-5493
CY  - Amsterdam [u.a.]
PB  - Elsevier Science
M1  - PreJuSER-57339
SP  - 1922 - 1927
PY  - 2006
N1  - Record converted from VDB: 12.11.2012
AB  - The irradiation test of HTR-10 spherical fuel elements was carried out in the Russian IVV-2M research reactor with the irradiation temperature of 1000 +/- 50 degrees C. After the burnup reached 100,000 MWd/t, the irradiation temperature was raised to a higher temperature. The high RIB levels observed during the normal irradiation test were due to manufacture defects of one to four coated particles. Post-irradiation examination indicated that at normal irradiation condition, the pyrolytic carbon (PyC) and silicon carbide (SiC) layers of particles kept their integrity. However, after irradiation at higher temperatures, several types of defects including radial and tangential cracks in SiC layers, cracks in buffer layers, and through coating failure were found, and the failure fraction reached 5.8 x 10(-2). These defects were most likely caused by the higher thermal stresses generated. In this study, PANAMA fuel performance code was used to estimate the heating temperature in the irradiation test. The calculated results showed that when the heating temperature is much higher than 1850 degrees C, the failure fraction of coated particle can reach the level of 1%. (c) 2006 Elsevier B.V All rights reserved.
KW  - J (WoSType)
LB  - PUB:(DE-HGF)16
UR  - <Go to ISI:>//WOS:000239529300009
DO  - DOI:10.1016/j.nucengdes.2006.01.018
UR  - https://juser.fz-juelich.de/record/57339
ER  -