000057453 245__ $$aSANS investigation of precipitate microstructure in nickel-base superalloys Waspaloy and DT750
000057453 260__ $$aMünchen$$bOldenbourg$$c2006
000057453 300__ $$a363 - 368
000057453 3367_ $$0PUB:(DE-HGF)16$$2PUB:(DE-HGF)$$aJournal Article
000057453 3367_ $$2DataCite$$aOutput Types/Journal article
000057453 3367_ $$00$$2EndNote$$aJournal Article
000057453 3367_ $$2BibTeX$$aARTICLE
000057453 3367_ $$2ORCID$$aJOURNAL_ARTICLE
000057453 3367_ $$2DRIVER$$aarticle
000057453 440_0 $$06017$$aZeitschrift für Kristallographie$$v$$x0044-2968$$ySuppl. 23
000057453 500__ $$aRecord converted from VDB: 12.11.2012
000057453 520__ $$aMicrostructure of Waspaloy and DT750 Ni-base superalloys was investigated after the heat treatment as well as after long thermal exposure by Small-Angle Neutron Scattering (SANS). The SANS results clearly showed that there are large differences even between samples of the DT750 superalloy produced using different facilities. The modified heat treatment used for DT750 suppressed the formation of secondary precipitates. A strong influence of the thermal exposure on the superalloy microstructure was observed which can have an impact on the mechanical properties.
000057453 536__ $$0G:(DE-Juel1)FUEK402$$2G:(DE-HGF)$$aRationelle Energieumwandlung$$cP12$$x0
000057453 588__ $$aDataset connected to Web of Science
000057453 650_7 $$2WoSType$$aJ
000057453 65320 $$2Author$$asuperalloys
000057453 65320 $$2Author$$aprecipitation
000057453 65320 $$2Author$$asmall-angle neutron scattering
000057453 7001_ $$0P:(DE-HGF)0$$aZrnik, J.$$b1
000057453 7001_ $$0P:(DE-Juel1)VDB41361$$aSeliga, T.$$b2$$uFZJ
000057453 7001_ $$0P:(DE-Juel1)VDB85249$$aPenkalla, H.-J.$$b3$$uFZJ
000057453 773__ $$0PERI:(DE-600)2546071-7$$a10.1524/zksu.2006.suppl_23.363$$gp. 363 - 368$$p363 - 368$$q363 - 368$$tZeitschrift für Kristallographie / Crystalline materials$$x0044-2968$$y2006
000057453 8567_ $$uhttp://dx.doi.org/10.1524/zksu.2006.suppl_23.363
000057453 909CO $$ooai:juser.fz-juelich.de:57453$$pVDB
000057453 9131_ $$0G:(DE-Juel1)FUEK402$$bEnergie$$kP12$$lRationelle Energieumwandlung$$vRationelle Energieumwandlung$$x0
000057453 9141_ $$aNachtrag$$y2006
000057453 915__ $$0StatID:(DE-HGF)0010$$aJCR/ISI refereed
000057453 9201_ $$0I:(DE-Juel1)VDB2$$d31.12.2006$$gIWV$$kIWV-2$$lWerkstoffstruktur und Eigenschaften$$x1
000057453 970__ $$aVDB:(DE-Juel1)90368
000057453 980__ $$aVDB
000057453 980__ $$aConvertedRecord
000057453 980__ $$ajournal
000057453 980__ $$aI:(DE-Juel1)IEK-2-20101013
000057453 980__ $$aUNRESTRICTED
000057453 981__ $$aI:(DE-Juel1)IMD-1-20101013
000057453 981__ $$aI:(DE-Juel1)IEK-2-20101013