000057840 1001_ $$0P:(DE-HGF)0$$aRubel, M. J.$$b0
000057840 245__ $$aOverview of comprehensive characterisation of erosion zones on plasma facing components
000057840 260__ $$aNew York, NY [u.a.]$$bElsevier$$c2006
000057840 300__ $$a
000057840 3367_ $$0PUB:(DE-HGF)16$$2PUB:(DE-HGF)$$aJournal Article
000057840 3367_ $$2DataCite$$aOutput Types/Journal article
000057840 3367_ $$00$$2EndNote$$aJournal Article
000057840 3367_ $$2BibTeX$$aARTICLE
000057840 3367_ $$2ORCID$$aJOURNAL_ARTICLE
000057840 3367_ $$2DRIVER$$aarticle
000057840 440_0 $$02169$$aFusion Engineering and Design$$v81$$x0920-3796$$y1
000057840 500__ $$aRecord converted from VDB: 12.11.2012
000057840 520__ $$aMorphology of carbon plasma facing components retrieved from the TEXTOR tokamak after long operation periods and exposure to total particle doses exceeding 7 x 10(26) m(-2) was determined. Emphasis was on the composition and structure of the erosion zones. Tiles from two limiters-the main toroidal belt pump ALT-II and auxiliary inner bumper-were examined using high-resolution microscopy, surface profilometry, ion beam analysis techniques and energy dispersive X-ray spectroscopy. The essence of results regarding the net-erosion zones is following: (i) microstructure of surfaces is significantly smoother than on a non-exposed graphite, whereas carbon fibre composites show similar appearance prior to the exposure and after; (ii) deuterium retention is 2-5 x 10(21) m(-2); (iii) the presence of plasma impurity atoms (e.g. metals) is detected predominantly in small cavities acting as local shadowed areas on the surface. The results are discussed in terms of processes of material erosion/re-deposition and tokamak operation conditions influencing the morphology of wall components. (c) 2005 Elsevier B.V. All rights reserved.
000057840 536__ $$0G:(DE-Juel1)FUEK402$$2G:(DE-HGF)$$aRationelle Energieumwandlung$$cP12$$x0
000057840 536__ $$0G:(DE-Juel1)FUEK403$$aFusion$$cP13$$x1
000057840 588__ $$aDataset connected to Web of Science
000057840 650_7 $$2WoSType$$aJ
000057840 65320 $$2Author$$agraphite
000057840 65320 $$2Author$$aerosion
000057840 65320 $$2Author$$aplasma facing components
000057840 65320 $$2Author$$afuel inventory
000057840 65320 $$2Author$$aTEXTOR
000057840 7001_ $$0P:(DE-HGF)0$$aFortuna, E.$$b1
000057840 7001_ $$0P:(DE-Juel1)130070$$aKreter, A.$$b2$$uFZJ
000057840 7001_ $$0P:(DE-Juel1)129810$$aWessel, E.$$b3$$uFZJ
000057840 7001_ $$0P:(DE-Juel1)VDB2741$$aPhilipps, V.$$b4$$uFZJ
000057840 7001_ $$0P:(DE-HGF)0$$aKurzydlowski, K. J.$$b5
000057840 773__ $$0PERI:(DE-600)1492280-0$$a10.1016/j.fusengdes.2005.07.037$$gVol. 81$$q81$$tFusion engineering and design$$v81$$x0920-3796$$y2006
000057840 8567_ $$uhttp://dx.doi.org/10.1016/j.fusengdes.2005.07.037
000057840 909CO $$ooai:juser.fz-juelich.de:57840$$pVDB
000057840 9131_ $$0G:(DE-Juel1)FUEK402$$bEnergie$$kP12$$lRationelle Energieumwandlung$$vRationelle Energieumwandlung$$x0
000057840 9131_ $$0G:(DE-Juel1)FUEK403$$bEnergie$$kP13$$lFusion$$vFusion$$x1
000057840 9141_ $$aNachtrag$$y2006
000057840 915__ $$0StatID:(DE-HGF)0010$$aJCR/ISI refereed
000057840 9201_ $$0I:(DE-Juel1)VDB181$$d31.12.2006$$gIPP$$kIPP$$lInstitut für Plasmaphysik$$x1
000057840 9201_ $$0I:(DE-Juel1)VDB2$$d31.12.2006$$gIWV$$kIWV-2$$lWerkstoffstruktur und Eigenschaften$$x2
000057840 970__ $$aVDB:(DE-Juel1)90966
000057840 980__ $$aVDB
000057840 980__ $$aConvertedRecord
000057840 980__ $$ajournal
000057840 980__ $$aI:(DE-Juel1)IEK-4-20101013
000057840 980__ $$aI:(DE-Juel1)IEK-2-20101013
000057840 980__ $$aUNRESTRICTED
000057840 981__ $$aI:(DE-Juel1)IMD-1-20101013
000057840 981__ $$aI:(DE-Juel1)IFN-1-20101013
000057840 981__ $$aI:(DE-Juel1)IEK-4-20101013
000057840 981__ $$aI:(DE-Juel1)IEK-2-20101013