TI  - Refinement of the Al-rich part of the Al-Cu-Re phase diagram and atomic model of the ternary Al$_{6.2}$Cu$_{2}$Re phase
JO  - Journal of alloys and compounds
VL  - 670
SN  - 0925-8388
CY  - Lausanne
PB  - Elsevier
M1  - FZJ-2017-01366
SP  - 18-24
PY  - 2016
AB  - Partial isothermal sections at 800, 650 and 590 °C were constructed for an Al-rich compositional range of Al–Cu–Re. The maximal solubility of Cu in the Al11Re4, h-Al4Re and l-Al4Re phases was found to be ∼6, 4.5, and 2.3 at% respectively, while the solubility of Re in the Al–Cu θ, η1 and ε2 phases was below 0.5 at%. Below 740 °C, a ternary hexagonal phase (P63, a = 1.1029 and c = 1.2746 nm) is formed in a small compositional range close to Al65Cu25Re10. Its structural model was deduced by direct methods applied on the precession electron diffraction tomography data.
LB  - PUB:(DE-HGF)16
UR  - <Go to ISI:>//WOS:000371765800003
DO  - DOI:10.1016/j.jallcom.2016.02.070
UR  - https://juser.fz-juelich.de/record/827168
ER  -