@ARTICLE{Song:839918,
      author       = {Song, Wenwen and Radulescu, Aurel and Liu, Lulu and Bleck,
                      Wolfgang},
      title        = {{S}tudy on a {H}igh {E}ntropy {A}lloy by {H}igh {E}nergy
                      {S}ynchrotron {X}-{R}ay {D}iffraction and {S}mall {A}ngle
                      {N}eutron {S}cattering},
      journal      = {Steel research international},
      volume       = {88},
      number       = {10},
      issn         = {1611-3683},
      address      = {Weinheim},
      publisher    = {Wiley-VCH73294},
      reportid     = {FZJ-2017-07496},
      pages        = {1700079},
      year         = {2017},
      abstract     = {In the present work, a quaternary CoCrFeNi high entropy
                      alloy (HEA) is investigated by means of high energy
                      synchrotron X-ray diffraction (SYXRD) and small angle
                      neutron scattering (SANS). At the as-forged state, the
                      microstructure of CoCrFeNi HEA is pure austenite. The
                      as-cast dendritic structure has been eliminated by the hot
                      forging at about 1100 °C and the average grain size
                      obtained is approximately 11.6 μm. The result shows
                      pronounced lattice distortion phenomenon in CoCrFeNi HEA,
                      which supposedly contributes to the solid solution
                      strengthening of the alloy. The CoCrFeNi HEA exhibits good
                      yield strength (Rp0.2 = 710 MPa at room temperature
                      and Rp0.2 = 660 MPa at 500 °C). The small angle
                      neutron scattering results further indicate the local
                      ordering effect in the fcc solid solution of CoCrFeNi HEA at
                      both room temperature and at 500 °C after tensile
                      deformation.},
      cin          = {JCNS (München) ; Jülich Centre for Neutron Science JCNS
                      (München) ; JCNS-FRM-II / Neutronenstreuung ; JCNS-1},
      ddc          = {620},
      cid          = {I:(DE-Juel1)JCNS-FRM-II-20110218 /
                      I:(DE-Juel1)JCNS-1-20110106},
      pnm          = {6G4 - Jülich Centre for Neutron Research (JCNS) (POF3-623)
                      / 6G15 - FRM II / MLZ (POF3-6G15)},
      pid          = {G:(DE-HGF)POF3-6G4 / G:(DE-HGF)POF3-6G15},
      experiment   = {EXP:(DE-MLZ)KWS2-20140101},
      typ          = {PUB:(DE-HGF)16},
      UT           = {WOS:000412176500009},
      doi          = {10.1002/srin.201700079},
      url          = {https://juser.fz-juelich.de/record/839918},
}