000851205 1001_ $$0P:(DE-HGF)0$$aUnocic, K. A.$$b0
000851205 245__ $$aHigh-temperature behavior of oxide dispersion strengthening CoNiCrAlY
000851205 260__ $$aAmsterdam [u.a.]$$bElsevier Science$$c2018
000851205 3367_ $$2DRIVER$$aarticle
000851205 3367_ $$2DataCite$$aOutput Types/Journal article
000851205 3367_ $$0PUB:(DE-HGF)16$$2PUB:(DE-HGF)$$aJournal Article$$bjournal$$mjournal$$s1534396771_23844
000851205 3367_ $$2BibTeX$$aARTICLE
000851205 3367_ $$2ORCID$$aJOURNAL_ARTICLE
000851205 3367_ $$00$$2EndNote$$aJournal Article
000851205 520__ $$aTo fabricate oxide dispersion strengthened bond coatings, commercial Co–30wt-%Ni–20Cr–8Al–0•4Y powder was milled with 2% additions of Al2O3, Y2O3 or Y2O3 + HfO2. Low-pressure plasma sprayed, free-standing specimens were oxidised in air + 10%H2O at 1100 °C both isothermally (100 h) and in 500, 1−h cycles. Dry air cyclic testing conducted at both ORNL and FZJ showed remarkably similar results. In general, the water vapour addition caused more scale spallation. Two LPPS specimens without oxide additions were tested for comparison. The specimens with 2%Al2O3 addition exhibited the best behaviour as the powder already contained 0•4%Y. Additions of 2%Y2O3 and especially 1%Y2O3 + 1%HfO2 resulted in over-doping as evidenced by high mass gains and the formation of Y- and Hf-rich pegs. Scanning transmission electron microscopy of the isothermal specimens showed no Hf and/or Y segregation to the alumina scale grain boundaries in the over-doped specimens.
000851205 536__ $$0G:(DE-HGF)POF3-113$$a113 - Methods and Concepts for Material Development (POF3-113)$$cPOF3-113$$fPOF III$$x0
000851205 588__ $$aDataset connected to CrossRef
000851205 7001_ $$0P:(DE-Juel1)159410$$aBergholz, J.$$b1
000851205 7001_ $$0P:(DE-Juel1)168207$$aHuang, T.$$b2$$ufzj
000851205 7001_ $$0P:(DE-Juel1)129766$$aNaumenko, D.$$b3$$ufzj
000851205 7001_ $$00000-0002-9165-3335$$aPint, B. A.$$b4$$eCorresponding author
000851205 7001_ $$0P:(DE-Juel1)129670$$aVaßen, R.$$b5$$ufzj
000851205 7001_ $$0P:(DE-Juel1)129782$$aQuadakkers, W. J.$$b6$$ufzj
000851205 773__ $$0PERI:(DE-600)2035150-1$$a10.1080/09603409.2017.1389423$$gVol. 35, no. 1-3, p. 108 - 119$$n1-3$$p108 - 119$$tMaterials at high temperatures$$v35$$x1878-6413$$y2018
000851205 909CO $$ooai:juser.fz-juelich.de:851205$$pVDB
000851205 9101_ $$0I:(DE-588b)5008462-8$$6P:(DE-Juel1)168207$$aForschungszentrum Jülich$$b2$$kFZJ
000851205 9101_ $$0I:(DE-588b)5008462-8$$6P:(DE-Juel1)129766$$aForschungszentrum Jülich$$b3$$kFZJ
000851205 9101_ $$0I:(DE-588b)5008462-8$$6P:(DE-Juel1)129670$$aForschungszentrum Jülich$$b5$$kFZJ
000851205 9101_ $$0I:(DE-588b)5008462-8$$6P:(DE-Juel1)129782$$aForschungszentrum Jülich$$b6$$kFZJ
000851205 9131_ $$0G:(DE-HGF)POF3-113$$1G:(DE-HGF)POF3-110$$2G:(DE-HGF)POF3-100$$3G:(DE-HGF)POF3$$4G:(DE-HGF)POF$$aDE-HGF$$bEnergie$$lEnergieeffizienz, Materialien und Ressourcen$$vMethods and Concepts for Material Development$$x0
000851205 9141_ $$y2018
000851205 915__ $$0StatID:(DE-HGF)0100$$2StatID$$aJCR$$bMATER HIGH TEMP : 2015
000851205 915__ $$0StatID:(DE-HGF)0200$$2StatID$$aDBCoverage$$bSCOPUS
000851205 915__ $$0StatID:(DE-HGF)0600$$2StatID$$aDBCoverage$$bEbsco Academic Search
000851205 915__ $$0StatID:(DE-HGF)0030$$2StatID$$aPeer Review$$bASC
000851205 915__ $$0StatID:(DE-HGF)0199$$2StatID$$aDBCoverage$$bThomson Reuters Master Journal List
000851205 915__ $$0StatID:(DE-HGF)0111$$2StatID$$aWoS$$bScience Citation Index Expanded
000851205 915__ $$0StatID:(DE-HGF)0150$$2StatID$$aDBCoverage$$bWeb of Science Core Collection
000851205 915__ $$0StatID:(DE-HGF)1160$$2StatID$$aDBCoverage$$bCurrent Contents - Engineering, Computing and Technology
000851205 915__ $$0StatID:(DE-HGF)9900$$2StatID$$aIF < 5
000851205 9201_ $$0I:(DE-Juel1)IEK-1-20101013$$kIEK-1$$lWerkstoffsynthese und Herstellungsverfahren$$x0
000851205 9201_ $$0I:(DE-Juel1)IEK-2-20101013$$kIEK-2$$lWerkstoffstruktur und -eigenschaften$$x1
000851205 980__ $$ajournal
000851205 980__ $$aVDB
000851205 980__ $$aI:(DE-Juel1)IEK-1-20101013
000851205 980__ $$aI:(DE-Juel1)IEK-2-20101013
000851205 980__ $$aUNRESTRICTED
000851205 981__ $$aI:(DE-Juel1)IMD-1-20101013
000851205 981__ $$aI:(DE-Juel1)IMD-2-20101013