%0 Journal Article
%A Gonzalez-Julian, Jesus
%A Go, Teresa
%A Mack, Daniel E.
%A Vaßen, Robert
%T Environmental resistance of Cr 2 AlC MAX phase under thermal gradient loading using a burner rig
%J Journal of the American Ceramic Society
%V 101
%N 5
%@ 0002-7820
%C Oxford [u.a.]
%I Wiley-Blackwell
%M FZJ-2018-04907
%P 1841 - 1846
%D 2018
%X Dense Cr2AlC materials were tested under a gradient loading for the first time using a burner rig. The severe thermal cycling conditions consist of 500 short cycles at 1200°C, with an accumulative time at the maximal temperature of more than 29 hours. The samples showed no visible damage under these conditions due to the formation of an outer protective α‐Al2O3 layer, which shows a strong adhesion with the Cr2AlC substrate. No cracks, delamination or damage were observed at the interface between the different layers. This excellent response under cyclic loading shows the excellent potential of Cr2AlC compounds for high‐temperature applications. 
%F PUB:(DE-HGF)16
%9 Journal Article
%U <Go to ISI:>//WOS:000426513900009
%R 10.1111/jace.15425
%U https://juser.fz-juelich.de/record/851207