      title        = {{M}icrostructure and secondary phases in epitaxial
                      {L}a{B}a{C}o 2 {O} 5.5+δ thin films},
      journal      = {Journal of materials science $\&$ technology},
      volume       = {34},
      number       = {2},
      issn         = {1005-0302},
      address      = {Shenyang},
      publisher    = {Ed. Board, Journal of Materials Science $\&$ Technology},
      reportid     = {FZJ-2019-01058},
      pages        = {398 - 402},
      year         = {2018},
      abstract     = {Aberration-corrected scanning transmission electron
                      microscopy was employed to investigate the microstructures
                      and secondary phases in LaBaCo2O5.5 + δ (LBCO) thin films
                      grown on SrTiO3 (STO) substrates. The as-grown films showed
                      an epitaxial growth on the substrates with atomically sharp
                      interfaces and orientation relationships of
                      [100]LBCO//[100]STO and (001)LBCO//(001)STO. Secondary
                      phases were observed in the films, which strongly depended
                      on the sample fabrication conditions. In the film prepared
                      at a temperature of 900 °C, nano-scale CoO pillars
                      nucleated on the substrate, and grew along the [001]
                      direction of the film. In the film grown at a temperature of
                      1000 °C, isolated nano-scale Co3O4 particles appeared,
                      which promoted the growth of {111} twinning structures in
                      the film. The orientation relationships and the interfaces
                      between the secondary phases and the films were illustrated,
                      and the growth mechanism of the film was discussed.},
      cin          = {ER-C-1},
      ddc          = {670},
      cid          = {I:(DE-Juel1)ER-C-1-20170209},
      pnm          = {143 - Controlling Configuration-Based Phenomena (POF3-143)},
      pid          = {G:(DE-HGF)POF3-143},
      typ          = {PUB:(DE-HGF)16},
      UT           = {WOS:000426447800020},
      doi          = {10.1016/j.jmst.2016.09.027},
      url          = {https://juser.fz-juelich.de/record/860283},
}