000877535 245__ $$aLifetime estimation of Cr2AlC MAX phase foam based on long-term oxidation and fracture mechanisms
000877535 260__ $$aAmsterdam$$bElsevier$$c2020
000877535 3367_ $$2DRIVER$$aarticle
000877535 3367_ $$2DataCite$$aOutput Types/Journal article
000877535 3367_ $$0PUB:(DE-HGF)16$$2PUB:(DE-HGF)$$aJournal Article$$bjournal$$mjournal$$s1592231110_31298
000877535 3367_ $$2BibTeX$$aARTICLE
000877535 3367_ $$2ORCID$$aJOURNAL_ARTICLE
000877535 3367_ $$00$$2EndNote$$aJournal Article
000877535 520__ $$aOxidation kinetics and mechanical behaviours of Cr2AlC foam with a porosity of 53 vol.% were investigated. Microstructures of Cr2AlC foams oxidised in the temperature range 1173 to 1473 K for times between 0 and 100 h were examined. Uniaxial compression tests were performed at different temperatures in the range 298–1398 K to assess mechanical properties. The oxidation formed cohesive Al2O3 layers on the Cr2AlC matrix, beneath which porous Cr7C3 was formed. The oxidation kinetics can be expressed by a parabolic law. An excessive oxidation took place first in thin struts, where a breakage Al2O3 layer occurred, followed by an oxygen inflow and decomposition of inner material. At 298 K, non-oxidised Cr2AlC foam fracured intergranularly. Slight oxidation improved compressive strength, as the Al2O3 layer (2.5 µm or thinner) can prevent cracks to propagate from inside outward. However, an excessive oxidation deteriorated any improvement due to the breakage of Al2O3 layer in thin struts followed by the material decomposition. At 1273 K and 1398 K, non-oxidised porous Cr2AlC fractured intergranularly, accompanied by a plastic deformation around small Al2O3 particles segregated at grain boundaries. Oxidised Cr2AlC foams with the Al2O3 thickness of 2.5 µm had a slightly higher brittle-to-plastic transition temperature (~1273 K) than dense Cr2AlC. A thicker Al2O3 layer (~5 µm) was required to reinforce the material due to inferior mechanical properties of Cr2AlC at high temperatures. On the basis of the elucidated oxidation and fracture mechanisms, a safety criterion for high-temperature applications was suggested.
000877535 536__ $$0G:(DE-HGF)POF3-113$$a113 - Methods and Concepts for Material Development (POF3-113)$$cPOF3-113$$fPOF III$$x0
000877535 588__ $$aDataset connected to CrossRef
000877535 7001_ $$0P:(DE-HGF)0$$aMatsumoto, Asato$$b1
000877535 7001_ $$0P:(DE-HGF)0$$aArai, Yoshio$$b2
000877535 7001_ $$0P:(DE-HGF)0$$aYamada, Noriyasu$$b3
000877535 7001_ $$0P:(DE-Juel1)129755$$aMalzbender, Jürgen$$b4
000877535 7001_ $$0P:(DE-Juel1)162271$$aGonzalez-Julian, Jesus$$b5
000877535 773__ $$0PERI:(DE-600)2953458-6$$a10.1016/j.mtla.2020.100718$$gVol. 12, p. 100718 -$$p100718 -$$tMaterialia$$v12$$x2589-1529$$y2020
000877535 8564_ $$uhttps://juser.fz-juelich.de/record/877535/files/Araki%20Materialia%202020.pdf$$yPublished on 2020-05-16. Available in OpenAccess from 2022-05-16.
000877535 8564_ $$uhttps://juser.fz-juelich.de/record/877535/files/Araki%20Materialia%202020.pdf?subformat=pdfa$$xpdfa$$yPublished on 2020-05-16. Available in OpenAccess from 2022-05-16.
000877535 909CO $$ooai:juser.fz-juelich.de:877535$$pdnbdelivery$$pdriver$$pVDB$$popen_access$$popenaire
000877535 9101_ $$0I:(DE-588b)5008462-8$$6P:(DE-Juel1)129755$$aForschungszentrum Jülich$$b4$$kFZJ
000877535 9101_ $$0I:(DE-588b)5008462-8$$6P:(DE-Juel1)162271$$aForschungszentrum Jülich$$b5$$kFZJ
000877535 9131_ $$0G:(DE-HGF)POF3-113$$1G:(DE-HGF)POF3-110$$2G:(DE-HGF)POF3-100$$3G:(DE-HGF)POF3$$4G:(DE-HGF)POF$$aDE-HGF$$bEnergie$$lEnergieeffizienz, Materialien und Ressourcen$$vMethods and Concepts for Material Development$$x0
000877535 9141_ $$y2020
000877535 915__ $$0StatID:(DE-HGF)0530$$2StatID$$aEmbargoed OpenAccess
000877535 915__ $$0StatID:(DE-HGF)0300$$2StatID$$aDBCoverage$$bMedline$$d2020-01-02
000877535 9201_ $$0I:(DE-Juel1)IEK-1-20101013$$kIEK-1$$lWerkstoffsynthese und Herstellungsverfahren$$x0
000877535 9201_ $$0I:(DE-Juel1)IEK-2-20101013$$kIEK-2$$lWerkstoffstruktur und -eigenschaften$$x1
000877535 9801_ $$aFullTexts
000877535 980__ $$ajournal
000877535 980__ $$aVDB
000877535 980__ $$aUNRESTRICTED
000877535 980__ $$aI:(DE-Juel1)IEK-1-20101013
000877535 980__ $$aI:(DE-Juel1)IEK-2-20101013
000877535 981__ $$aI:(DE-Juel1)IMD-1-20101013
000877535 981__ $$aI:(DE-Juel1)IMD-2-20101013