000905787 1001_ $$0P:(DE-Juel1)177016$$aRoitzheim, Christoph$$b0$$ufzj
000905787 1112_ $$aECS PRiME 2020$$conline$$d2020-10-04 - 2020-10-09$$wUSA
000905787 245__ $$aModified Cathode Materials for Garnet Based All-Solid-State Lithium Batteries
000905787 260__ $$c2020
000905787 3367_ $$033$$2EndNote$$aConference Paper
000905787 3367_ $$2DataCite$$aOther
000905787 3367_ $$2BibTeX$$aINPROCEEDINGS
000905787 3367_ $$2DRIVER$$aconferenceObject
000905787 3367_ $$2ORCID$$aLECTURE_SPEECH
000905787 3367_ $$0PUB:(DE-HGF)6$$2PUB:(DE-HGF)$$aConference Presentation$$bconf$$mconf$$s1649226573_24211$$xOther
000905787 520__ $$aAll solid-state batteries (ASB) are an emerging energy storage technology, which is expected to improve the safety on the cell level and to increase the battery energy density. One of important issues in the development of bulk-type ASBs with a high energy density is a possibility of processing thick composites cathodes with percolating pathways for ion and electron transport. For the ceramic electrolytes such as garnet-type Ta-substituted LLZ (Li6.6La3Zr1.6Ta0.4O12; LLZ:Ta) the practical realization of composite cathodes is however challenging due to the necessity of high temperature processing, raising the issues of material compatibility and the formation of reaction interphases influencing the total cell resistance. So far, the thick garnet-based composite cathodes could be made only with LiCoO2 (LCO) as an active material. For this kind of ASB, high areal capacities of up to 1.63 mAh/cm² were obtained. However, the utilization of high capacity cathode materials like LiNixCoyMn1–x–yO2 (NCM) was so far not possible due to the lower thermal stability of NCM as compared to LCO and the resulting enhanced reactivity between LLZ:Ta and NCM.Usually NCM materials were only optimized for liquid electrolyte based batteries. Therefore, an optimization of these active materials with respect to their integration into ASBs is intended in this work. Possible strategies for this optimization are doping or substitution, surface coatings or core-shell structures.We present the synthesis of optimized cathode materials for bulk-type, fully inorganic ASBs based on ceramic materials. A detailed material screening of NCM materials with different compositions and modifications is performed by evaluating the compatibility with cubic LLZ:Ta during co-sintering at elevated temperatures. The compatibility is tested by in situ high temperature X-ray diffraction (HT-XRD), differential thermal analysis/thermogravimetry (DTA/TG), Raman spectroscopy and X-ray photoelectron spectroscopy (XPS). The experimental work is supported by simulation studies using ab-initio-based approaches such as density functional theory (DFT), ab initio molecular dynamics (AIMD) as well as ab initio atomistic thermodynamics and kinetics approaches. These simulation based methods enable the prediction of lattice parameter of NCM at different stages of charge. Additionally, the calculation of interchange energies needed for the cation interchange between NCM and cubic LLZ:Ta during co-sintering is possible.Boron doping of NCM was investigated as a possible strategy to improve its compatibility with LLZ:Ta, as this strategy was demonstrated to be very efficient for liquid electrolytes. The theoretical and experimental results on B-doped NCM with different compositions are already available. However, the formation of secondary phases after co-sintering that was predicted by us theoretically and confirmed experimentally using Rietveld refinement discard boron doping as a way to enhance thermal stability of NCM during the co-sintering with cubic LLZ:Ta. Introduction of other dopants and surface coatings is currently investigated to improve the compatibility of NCM with cubic LLZ:Ta during co-sintering. The combined experimental and theoretical approach is expected to result in an optimized cathode material for ASBs with enhanced performance.
000905787 536__ $$0G:(DE-HGF)POF4-1221$$a1221 - Fundamentals and Materials (POF4-122)$$cPOF4-122$$fPOF IV$$x0
000905787 536__ $$0G:(BMBF)03EK3054A$$aVerbundvorhaben SimCaMat: Modellierung und Synthese verbesserter Kathodenmaterialien (03EK3054A)$$c03EK3054A$$x1
000905787 588__ $$aDataset connected to CrossRef, Journals: juser.fz-juelich.de
000905787 7001_ $$0P:(DE-Juel1)145623$$aFinsterbusch, Martin$$b1$$eCorresponding author$$ufzj
000905787 7001_ $$0P:(DE-Juel1)174502$$aKaghazchi, Payam$$b2$$ufzj
000905787 7001_ $$0P:(DE-Juel1)171780$$aFattakhova-Rohlfing, Dina$$b3
000905787 773__ $$a10.1149/MA2020-025987mtgabs$$gVol. MA2020-02, no. 5, p. 987 - 987$$y2020
000905787 8564_ $$uhttps://juser.fz-juelich.de/record/905787/files/Abstract_ECSprime_CR_20200405_DF.pdf$$yOpenAccess
000905787 909CO $$ooai:juser.fz-juelich.de:905787$$pdriver$$pVDB$$popen_access$$popenaire
000905787 9101_ $$0I:(DE-588b)5008462-8$$6P:(DE-Juel1)177016$$aForschungszentrum Jülich$$b0$$kFZJ
000905787 9101_ $$0I:(DE-HGF)0$$6P:(DE-Juel1)177016$$a Universität Duisburg-Essen$$b0
000905787 9101_ $$0I:(DE-588b)5008462-8$$6P:(DE-Juel1)145623$$aForschungszentrum Jülich$$b1$$kFZJ
000905787 9101_ $$0I:(DE-588b)5008462-8$$6P:(DE-Juel1)174502$$aForschungszentrum Jülich$$b2$$kFZJ
000905787 9101_ $$0I:(DE-588b)5008462-8$$6P:(DE-Juel1)171780$$aForschungszentrum Jülich$$b3$$kFZJ
000905787 9101_ $$0I:(DE-HGF)0$$6P:(DE-Juel1)171780$$a Universität Duisburg-Essen$$b3
000905787 9131_ $$0G:(DE-HGF)POF4-122$$1G:(DE-HGF)POF4-120$$2G:(DE-HGF)POF4-100$$3G:(DE-HGF)POF4$$4G:(DE-HGF)POF$$9G:(DE-HGF)POF4-1221$$aDE-HGF$$bForschungsbereich Energie$$lMaterialien und Technologien für die Energiewende (MTET)$$vElektrochemische Energiespeicherung$$x0
000905787 915__ $$0StatID:(DE-HGF)0510$$2StatID$$aOpenAccess
000905787 920__ $$lyes
000905787 9201_ $$0I:(DE-Juel1)IEK-1-20101013$$kIEK-1$$lWerkstoffsynthese und Herstellungsverfahren$$x0
000905787 9801_ $$aFullTexts
000905787 980__ $$aconf
000905787 980__ $$aVDB
000905787 980__ $$aUNRESTRICTED
000905787 980__ $$aI:(DE-Juel1)IEK-1-20101013
000905787 981__ $$aI:(DE-Juel1)IMD-2-20101013