Abstract: New oxygen transport membrane materials based on SrTi1-xFexO3-δ, synthesized through solid state reaction and processed via tape casting were characterized with respect to their mechanical behaviour via depth-sensitive indentation and ring-on-ring flexural testing. The elastic moduli obtained by indentation with 1 N load for SrTi1-xFexO3-δ (x = 0.25, 0.35, 0.5) specimens were 147 ± 10 GPa, 123 ± 6 GPa and 158 ± 10 GPa, respectively. Fracture stress was accessed by ring-on-ring testing performed at 100 N/min and the obtained results were 92 ± 9 MPa, 117 ± 15 MPa, and 100 ± 15 MPa for SrTi0.75Fe0.25O3, SrTi0.65Fe0.35O3, and SrTi0.5Fe0.5O3 respectively. Ring-on-ring tests conducted at different loading rates gave access to subcritical crack growth sensitivity and aided the prediction of the materials’ lifetime through stress-time-probability diagrams, where SrTi1-xFexO3-δ (x = 0.25, 0.35, 0.5) may resist for 1 year with a failure probability of 0.1% at least 15 MPa, 22 MPa, and 12 MPa respectively.
Keyword(s): Engineering, Industrial Materials and Processing (1st) ; Materials Science (2nd)
; Current Contents - Engineering, Computing and Technology ; Current Contents - Physical, Chemical and Earth Sciences ; Ebsco Academic Search ; IF < 5 ; JCR ; SCOPUS ; Science Citation Index ; Science Citation Index Expanded ; Thomson Reuters Master Journal List ; Web of Science Core Collection
|
The record appears in these collections: |
PDF