TY  - JOUR
AU  - Gonzalez-Julian, Jesus
AU  - Onrubia, Sara
AU  - Bram, Martin
AU  - Broeckmann, Christoph
AU  - Vassen, Robert
AU  - Guillon, Olivier
TI  - High-temperature oxidation and compressive strength of Cr2AlC MAX phase foams with controlled porosity
JO  - Journal of the American Ceramic Society
VL  - 101
IS  - 2
SN  - 0002-7820
CY  - Oxford [u.a.]
PB  - Wiley-Blackwell
M1  - FZJ-2018-00198
SP  - 542 - 552
PY  - 2018
AB  - Cr2AlC foams have been processed for the first time containing low (35 vol%), intermediate (53 vol%), and high (75 vol%) content of porosity and three ranges of pore size, 90-180 μm, 180-250 μm, and 250-400 μm. Sacrificial template technique was used as the processing method, utilizing NH4HCO3 as a temporary pore former. Cr2AlC foams exhibited negligible oxidation up to 800°C and excellent response up to 1300°C due to the in-situ formation of an outer thin continuous protective layer of α-Al2O3. The in-situ α-Al2O3 protective layer covered seamlessly all the external surface of the pores, even when they present sharp angles and tight corners, reducing significantly the further oxidation of the foams. The compressive strength of the foams was 73 and 13 MPa for 53 vol% and 75 vol% porosity, respectively, which increased up to 128 and 24 MPa after their oxidation at 1200°C for 1 hour. The increase in the compressive strength after the oxidation was caused by the switch from inter- to transgranular fracture mode. According to the excellent high-temperature response, heat exchangers and catalyst supports are the potential application of these foams.
LB  - PUB:(DE-HGF)16
UR  - <Go to ISI:>//WOS:000416933700008
DO  - DOI:10.1111/jace.15224
UR  - https://juser.fz-juelich.de/record/841901
ER  -