%T Role of Temperature in Na 2 SO 4 –K 2 SO 4 Deposit Induced Type II Hot Corrosion of NiAl Coating on a Commercial Ni‐Based Superalloy
%J Advanced engineering materials
%V 22
%N 6
%@ 1527-2648
%C Frankfurt, M.
%I Deutsche Gesellschaft für Materialkunde
%M FZJ-2020-01947
%P 1901244
%D 2020
%X The life span of gas turbine coatings may be restricted by type II hot corrosion when exposed at elevated temperatures in aggressive environments during service. Herein, the temperature dependence of corrosion morphologies and kinetics of NiAl coating on a second‐generation single crystalline Ni‐based superalloy is studied to provide an insight into the possible corrosion mechanisms. A series of tests are performed at 600–800 °C in air‐300 ppm SO2 atmosphere with Na2SO4–20% K2SO4 salt mixture as deposit. Severe attack is observed at both 700 and 750 °C after 24 h exposure, whereas at 600 and 800 °C, only a minor attack is found. The results indicate that the corrosion rate is strongly governed by Na2SO4–NiSO4 liquid formation, and temperature affects the attack rate of the outer coating (mainly β‐NiAl phase) primarily by changing the required minimum SO3 partial pressure to stabilize this liquid. The influence of temperature and 𝑝SO3 on phase equilibrium of the salt and oxide mixture is calculated with an in‐house developed thermodynamic database. The predicted minimum 𝑝SO3 for liquid formation calculated with the database is consistent with the experimental results. 
%F PUB:(DE-HGF)16
%9 Journal Article
%U <Go to ISI:>//WOS:000514743600001
%R 10.1002/adem.201901244
%U https://juser.fz-juelich.de/record/875316