245 _ _ |a Combined κ-carbide precipitation and recovery enables ultra-high strength and ductility in light-weight steels
260 _ _ |a Amsterdam
|c 2020
|b Elsevier
336 7 _ |a article
|2 DRIVER
336 7 _ |a Output Types/Journal article
|2 DataCite
336 7 _ |a Journal Article
|b journal
|m journal
|0 PUB:(DE-HGF)16
|s 1609850171_18366
|2 PUB:(DE-HGF)
336 7 _ |a ARTICLE
|2 BibTeX
336 7 _ |a JOURNAL_ARTICLE
|2 ORCID
336 7 _ |a Journal Article
|0 0
|2 EndNote
520 _ _ |a Light-weight high-manganese steels with high aluminum and carbon contents are known to possess high age-hardening potential due to the precipitation of nano-sized κ-carbides. Although in recrystallized material the precipitation of the κ-phase has been widely researched, the influence of pre-deformation/deformation microstructure on the formation of κ-carbides is still unknown. The present study aims at gaining an increased understanding of the underlying mechanisms (and their interplay) active during annealing after pre-deformation, i.e. concurrent strengthening by precipitation of κ-carbides and softening by recovery/recrystallization. Therefore, a Fe-29.8Mn-7.65Al-1.11C steel was age-hardened in deformed/cold-rolled as well as in recrystallized condition. The microstructure and tensile behavior of the material in both states after annealing treatments at 600–800 °C were investigated by means of light optical microscopy, (high-resolution) scanning transmission electron microscopy, x-ray diffraction and hardness measurements as well as tensile tests. The focus was put on understanding the interplay between microstructural defects (e.g. dislocations), precipitation of κ-carbides, and recovery/recrystallization. The fundamental dependence of strengthening and softening mechanisms on the precondition, annealing parameters and correlation with the mechanical properties are discussed.
536 _ _ |a 143 - Controlling Configuration-Based Phenomena (POF3-143)
|0 G:(DE-HGF)POF3-143
|c POF3-143
|x 0
|f POF III
536 _ _ |a DFG project 29898171 - SFB 761: Stahl - ab initio. Quantenmechanisch geführtes Design neuer Eisenbasis-Werkstoffe (29898171)
|0 G:(GEPRIS)29898171
|c 29898171
|x 1
588 _ _ |a Dataset connected to CrossRef
700 1 _ |a Haase, Christian
|0 P:(DE-HGF)0
|b 1
700 1 _ |a Lipińska-Chwałek, Marta
|0 P:(DE-HGF)0
|b 2
700 1 _ |a Mayer, Joachim
|0 P:(DE-Juel1)130824
|b 3
700 1 _ |a Molodov, Dmitri A.
|0 P:(DE-HGF)0
|b 4
773 _ _ |a 10.1016/j.msea.2020.139928
|g Vol. 795, p. 139928 -
|0 PERI:(DE-600)2012154-4
|p 139928 -
|t Materials science and engineering / A
|v 795
|y 2020
|x 0921-5093
856 4 _ |u https://juser.fz-juelich.de/record/888762/files/MSEA-D-20-01628%20%282%29%5B1%5D-submited-1.pdf
|y Published on 2020-07-23. Available in OpenAccess from 2022-07-23.
909 C O |o oai:juser.fz-juelich.de:888762
|p openaire
|p open_access
|p VDB
|p driver
|p dnbdelivery
910 1 _ |a Forschungszentrum Jülich
|0 I:(DE-588b)5008462-8
|k FZJ
|b 2
|6 P:(DE-HGF)0
910 1 _ |a RWTH Aachen
|0 I:(DE-588b)36225-6
|k RWTH
|b 2
|6 P:(DE-HGF)0
910 1 _ |a Forschungszentrum Jülich
|0 I:(DE-588b)5008462-8
|k FZJ
|b 3
|6 P:(DE-Juel1)130824
913 1 _ |a DE-HGF
|b Energie
|l Future Information Technology - Fundamentals, Novel Concepts and Energy Efficiency (FIT)
|1 G:(DE-HGF)POF3-140
|0 G:(DE-HGF)POF3-143
|3 G:(DE-HGF)POF3
|2 G:(DE-HGF)POF3-100
|4 G:(DE-HGF)POF
|v Controlling Configuration-Based Phenomena
|x 0
914 1 _ |y 2020
915 _ _ |a DBCoverage
|0 StatID:(DE-HGF)0200
|2 StatID
|b SCOPUS
|d 2020-08-31
915 _ _ |a DBCoverage
|0 StatID:(DE-HGF)0160
|2 StatID
|b Essential Science Indicators
|d 2020-08-31
915 _ _ |a DBCoverage
|0 StatID:(DE-HGF)1160
|2 StatID
|b Current Contents - Engineering, Computing and Technology
|d 2020-08-31
915 _ _ |a DBCoverage
|0 StatID:(DE-HGF)0600
|2 StatID
|b Ebsco Academic Search
|d 2020-08-31
915 _ _ |a Creative Commons Attribution-NonCommercial-NoDerivs CC BY-NC-ND 4.0
|0 LIC:(DE-HGF)CCBYNCND4
|2 HGFVOC
915 _ _ |a Embargoed OpenAccess
|0 StatID:(DE-HGF)0530
|2 StatID
915 _ _ |a JCR
|0 StatID:(DE-HGF)0100
|2 StatID
|b MAT SCI ENG A-STRUCT : 2018
|d 2020-08-31
915 _ _ |a WoS
|0 StatID:(DE-HGF)0113
|2 StatID
|b Science Citation Index Expanded
|d 2020-08-31
915 _ _ |a DBCoverage
|0 StatID:(DE-HGF)0150
|2 StatID
|b Web of Science Core Collection
|d 2020-08-31
915 _ _ |a IF < 5
|0 StatID:(DE-HGF)9900
|2 StatID
|d 2020-08-31
915 _ _ |a Peer Review
|0 StatID:(DE-HGF)0030
|2 StatID
|b ASC
|d 2020-08-31
915 _ _ |a DBCoverage
|0 StatID:(DE-HGF)1150
|2 StatID
|b Current Contents - Physical, Chemical and Earth Sciences
|d 2020-08-31
915 _ _ |a DBCoverage
|0 StatID:(DE-HGF)0300
|2 StatID
|b Medline
|d 2020-08-31
915 _ _ |a DBCoverage
|0 StatID:(DE-HGF)0199
|2 StatID
|b Clarivate Analytics Master Journal List
|d 2020-08-31
920 _ _ |l yes
920 1 _ |0 I:(DE-Juel1)ER-C-2-20170209
|k ER-C-2
|l Materialwissenschaft u. Werkstofftechnik
|x 0
980 _ _ |a journal
980 _ _ |a VDB
980 _ _ |a UNRESTRICTED
980 _ _ |a I:(DE-Juel1)ER-C-2-20170209
980 1 _ |a FullTexts


LibraryCollectionCLSMajorCLSMinorLanguageAuthor
Marc 21