| Hauptseite > Publikationsdatenbank > Size-Dependent Phase Transformations in Bismuth Oxide Nanoparticles. II. Melting and Stability Diagram |
| Hauptseite > Publikationsdatenbank > Size-Dependent Phase Transformations in Bismuth Oxide Nanoparticles. II. Melting and Stability Diagram |
| Journal Article | FZJ-2015-00656 |
; ;
2014
Soc.
Washington, DC
This record in other databases: 
Please use a persistent id in citations: doi:10.1021/jp509841s
Abstract: Melting of nanocrystalline bismuth oxide particles between 6 and 50 nm was investigated in situ in the transmission electron microscope (TEM). It revealed a size-dependent melting behavior with a strong melting point reduction (−55% at 6 nm). One reason is a −230 K offset in the bulk melting temperature which is apparently caused by the β-phase in which the nanomaterial resides. As a second reason, a strong size dependency was observed from which an approximate solid-surface energy of 0.3 J/m2 was determined. Yet, the conditions in the TEM could cause a lowering of the transition temperatures compared to chemically neutral conditions, although theoretical considerations predict reduction in the solid state to be negligible. Everything indicates that no stable, liquid surface layer forms prior to melting. In spite of the covalent-ionic bonds in this oxide material the qualitatively same size dependence shows like in metals. Combined with size-dependent evaporation examined in a companion study
; Current Contents - Physical, Chemical and Earth Sciences ; IF < 5 ; JCR ; SCOPUS ; Science Citation Index ; Science Citation Index Expanded ; Thomson Reuters Master Journal List ; Web of Science Core Collection
|
The record appears in these collections: |
PDF