Tanner, J. ; Bläsing, M.FZJ* ; Müller, M.FZJ* ; Bhattacharya, S. (Corresponding author)

2016
American Chemical Society Columbus, Ohio

This record in other databases:  

Please use a persistent id in citations: doi:10.1021/acs.energyfuels.5b03012

Abstract: The reactions and transformations of mineral and nonmineral inorganic species in Victorian (MOR) and Rhenish (HKT) coals were investigated in a two-stage process under high temperature, entrained flow pyrolysis, and gasification conditions. The parent coals were pyrolyzed at a temperature between 1100 and 1400 °C in 100 vol % nitrogen. The resulting char samples were collected and gasified at their corresponding pyrolysis temperatures in 10–80 vol % CO2 in N2. Low temperature (500 °C) ash subsamples from the parent coals, chars, and gasification residues were analyzed for elemental and mineral phase composition. The phase composition analysis was in agreement with the proportions of various inorganic constituents in the elemental analysis. In general, the extent of reaction and phase transformation increased with increasing temperature and carbon conversion, which is related to increasing temperature and CO2 concentration. The char elemental and phase compositions were similar to those of the corresponding parent coal and consisted predominantly of SiO2, CaSO4, and CaCO3 with minor amounts of MgO and Fe2O3 in the MOR samples. Char gasification resulted in consistently increasing reaction and transformation trends, which indicates that thermodynamic equilibrium was not reached. Low temperature gasification of MOR and HKT char samples resulted predominantly in thermal decomposition of CaSO4, retention of CaCO3 due to recarbonation, and formation of MgO. The ash composition at high temperature differed based on the amounts of and reactions between various parent coal inorganic constituents. In particular, the fate of Ca and Mg differed markedly between the two coals. For MOR, decomposition of MgO resulted in depletion of Mg at high temperatures, whereas Mg was retained in HKT gasification residues as MgAl2O4 and Ca2MgSi2O7 due to higher Si and Al content. CaO from CaSO4 and CaCO3 decomposition was retained in MOR samples as Ca2Fe2O5 and Ca2SiO4, and in HKT as Ca2MgSi2O7.

---

Contributing Institute(s):

1. Werkstoffstruktur und -eigenschaften (IEK-2)

Research Program(s):

1. 111 - Efficient and Flexible Power Plants (POF3-111) (POF3-111)

Appears in the scientific report 2016

---

Database coverage:
; Current Contents - Engineering, Computing and Technology ; IF < 5 ; JCR ; NCBI Molecular Biology Database ; Nationallizenz ; No Authors Fulltext ; SCOPUS ; Science Citation Index ; Science Citation Index Expanded ; Thomson Reuters Master Journal List ; Web of Science Core Collection

---