Performance and Degradation of a SOEC Stack with Different Cell Components

Yan, Yulin; Blum, Ludger; Lehnert, Werner; Fang, Qingping

doi:10.1016/j.electacta.2017.11.180

Journal Article

FZJ-2017-07704

Performance and Degradation of a SOEC Stack with Different Cell Components

Yan, Y. (Corresponding author)FZJ* ; Fang, Q.FZJ* ; Blum, L.FZJ* ; Lehnert, W.FZJ*

2017
Elsevier New York, NY [u.a.]

Electrochimica acta 258, 1254 - 1261 (2017) [10.1016/j.electacta.2017.11.180]

This record in other databases:

Please use a persistent id in citations: doi:10.1016/j.electacta.2017.11.180

Abstract: High temperature water electrolysis with solid oxide electrolysis cells (SOECs) is a promising method for hydrogen production. In order to study the performance and degradation behavior of cells with different cell components in electrolysis mode, a four-cell stack was assembled that used JÜLICH's F10 design with two types of air electrodes based on La0.6Sr0.4CoO3−δ (LSC) and La0.6Sr0.4Co0.2Fe0.8O3−δ (LSCF). A PVD-prepared GDC layer was applied to LSCF cells while a screen-printing GDC layer was used in the LSC cells. The performance of the stack was first characterized with IV-curve measurements in both SOFC and SOEC modes within the temperature range of 700–800 °C. The durability of the stack was investigated by conducting a long-term stationary electrolysis operation with a constant current density of −0.5 Acm−2 and steam conversion rate of 50% at 800 °C. Electrochemical Impedance Spectroscopy (EIS) was used to study the electrochemical performance of the stack, as well as the degradation behavior during long-term electrolysis operation. The method “Distribution of Relaxation Times” (DRT) was applied for the further analysis of the EIS data, and the DRT results have successfully supported the stack degradation analysis.

Classification: