http://join2-wiki.gsi.de/foswiki/pub/Main/Artwork/join2_logo100x88.png Performance of YSZ and Gd2Zr2O7/YSZ double layer thermal barrier coatings in burner rig tests

Vaßen, R. (Corresponding author)FZJ* ; Bakan, E.FZJ* ; Mack, D.FZJ* ; Schwartz-Lückge, S.FZJ* ; Sebold, D.FZJ* ; Sohn, Y. J.FZJ* ; Zhou, D. ; Guillon, O.FZJ*

2020
Elsevier Science Amsterdam [u.a.]

This record in other databases:    

Please use a persistent id in citations: http://hdl.handle.net/2128/23715  doi:10.1016/j.jeurceramsoc.2019.10.021

Abstract: Double layer thermal barrier coatings (TBCs) consisting of a Gd2Zr2O7 (GZO) top and an ytrria stabilized zirconia (YSZ) interlayer have been tested in a burner rig facility and the results compared to the ones of conventional YSZ single layers. In order to gain insight in the high temperature capability of the alternative TBC material, high surface temperatures of up to 1550 °C have been chosen while keeping the bond coat temperature similar. It turned out that the performance of all systems is largely depending on the microstructure of the coatings especially reduced porosity levels of GZO being detrimental. In addition, it was more difficult in GZO than in YSZ coatings to obtain highly porous and still properly bonded microstructures. Another finding was the reduced lifetime with increasing surface temperatures, the amount of reduction is depending on the investigated system. The reasons for this behavior are analyzed and discussed in detail.

---

Contributing Institute(s):

1. Werkstoffsynthese und Herstellungsverfahren (IEK-1)
2. JARA-ENERGY (JARA-ENERGY)

Research Program(s):

1. 113 - Methods and Concepts for Material Development (POF3-113) (POF3-113)

Appears in the scientific report 2019

---

Database coverage:
; ; Clarivate Analytics Master Journal List ; Current Contents - Engineering, Computing and Technology ; Current Contents - Physical, Chemical and Earth Sciences ; Ebsco Academic Search ; IF < 5 ; JCR ; SCOPUS ; Science Citation Index ; Science Citation Index Expanded ; Web of Science Core Collection

---