http://join2-wiki.gsi.de/foswiki/pub/Main/Artwork/join2_logo100x88.png Analysis of the Thermomechanical Fatigue Behavior of Fully Ferritic High Chromium Steel Crofer®22 H with Cyclic Indentation Testing

Blinn, B. (Corresponding author) ; Görzen, D. ; Fischer, T.FZJ* ; Kuhn, B.FZJ* ; Beck, T.

2020
MDPI Basel

This record in other databases:  

Please use a persistent id in citations: doi:10.3390/app10186461  doi:10.34734/FZJ-2020-03169

Abstract: The 22 wt.% Cr, fully ferritic stainless steel Crofer®22 H has higher thermomechanical fatigue (TMF)- lifetime compared to advanced ferritic-martensitic P91, which is assumed to be caused by different damage tolerance, leading to differences in crack propagation and failure mechanisms. To analyze this, instrumented cyclic indentation tests (CITs) were used because the material’s cyclic hardening potential—which strongly correlates with damage tolerance, can be determined by analyzing the deformation behavior in CITs. In the presented work, CITs were performed for both materials at specimens loaded for different numbers of TMF-cycles. These investigations show higher damage tolerance for Crofer®22 H and demonstrate changes in damage tolerance during TMF-loading for both materials, which correlates with the cyclic deformation behavior observed in TMF-tests. Furthermore, the results obtained at Crofer®22 H indicate an increase of damage tolerance in the second half of TMF-lifetime, which cannot be observed for P91. Moreover, CITs were performed at Crofer®22 H in the vicinity of a fatigue crack, enabling to locally analyze the damage tolerance. These CITs show differences between crack edges and the crack tip. Conclusively, the presented results demonstrate that CITs can be utilized to analyze TMF-induced changes in damage tolerance.

---

Contributing Institute(s):

1. Werkstoffstruktur und -eigenschaften (IEK-2)

Research Program(s):

1. 1243 - Thermal Energy Storage (POF4-124) (POF4-124)

---

Database coverage:
; ; ; ; Article Processing Charges ; Clarivate Analytics Master Journal List ; Current Contents - Engineering, Computing and Technology ; Current Contents - Physical, Chemical and Earth Sciences ; DOAJ Seal ; Essential Science Indicators ; Fees ; IF < 5 ; JCR ; NCBI Molecular Biology Database ; SCOPUS ; Science Citation Index Expanded ; Web of Science Core Collection

---