http://join2-wiki.gsi.de/foswiki/pub/Main/Artwork/join2_logo100x88.png Effect of rhenium on defects evolution behavior in tungsten under irradiation

Wang, Z. ; Gao, L. (Corresponding author)FZJ* ; Zhu, X.-L. ; Yuan, Y. ; Wang, S. ; Cheng, L. ; Lu, G.-H.

2021
IAEA Vienna

This record in other databases:    

Please use a persistent id in citations: doi:10.1088/1741-4326/abd920  doi:10.34734/FZJ-2021-05656

Abstract: The influence of the transmutation element rhenium (Re) on defect evolution in tungsten (W) during irradiations with heavy ions and deuterium (D) plasma was investigated. Rolled W and W–5Re alloy (Re concentration 5 wt.%) were irradiated with 500 keV iron ions to 0.06 and 0.6 dpa (displacement per atom), and deuterium plasma at 38 eV/D to a fluence of 2.2 × 1025 D m−2 at ∼373 K. The results of Doppler broadening spectroscopy by the positron annihilation technique indicate that more or larger vacancy-type defects were produced in W than in the W–5Re during Fe ion irradiation, suggesting the important role of Re on inhibiting the migration and/or clustering of vacancies. The much smaller and shallower blistering in W–5Re than in W after the same D plasma exposure points to the pinning effects on dislocations by Re. The total retained D amounts in W–5Re and W materials are comparable, but with very different concentration profile at corresponding depth. This is explained by the blister formation exerting influence on the D inward diffusion. Demonstrating the important role of Re on the defect evolution in W under irradiation, the present work provides an enhanced understanding on the possible effects of neutron irradiation on the performance of plasma-facing materials in future fusion devices.

---

Contributing Institute(s):

1. Plasmaphysik (IEK-4)

Research Program(s):

1. 134 - Plasma-Wand-Wechselwirkung (POF4-134) (POF4-134)

---

Database coverage:
; Clarivate Analytics Master Journal List ; Current Contents - Physical, Chemical and Earth Sciences ; Ebsco Academic Search ; Essential Science Indicators ; IF < 5 ; JCR ; National-Konsortium ; Nationallizenz ; SCOPUS ; Science Citation Index Expanded ; Web of Science Core Collection

---