Structure and thermoelectric properties of EuTi(O,N)3 ± δ

Sagarna, L.; Rushchanskii, K. Z.; Ležaić, M.; Weidenkaff, A.; Waser, R.; Yoon, S.; Maegli, A.; Populoh, S.; Shkabko, A.; Pokrant, S.

doi:10.1063/1.4813098

Journal Article

FZJ-2013-03175

Structure and thermoelectric properties of EuTi(O,N)3 ± δ

Sagarna, L. (Corresponding author) ; Rushchanskii, K. Z. ; Maegli, A. ; Yoon, S. ; Populoh, S. ; Shkabko, A.FZJ* ; Pokrant, S. ; Ležaić, M.FZJ* ; Waser, R.FZJ* ; Weidenkaff, A.

2013
American Institute of Physics Melville, NY

Journal of applied physics 114(3), 033701 - (2013) [10.1063/1.4813098]

This record in other databases:

Please use a persistent id in citations: http://hdl.handle.net/2128/16814 doi:10.1063/1.4813098

Abstract: After partial substitution of nitrogen for oxygen in EuTiO3, the crystal structure, thermoelectric properties, morphology, and electronic structure of the products were analyzed and compared with pristine EuTiO3. The space group of EuTi(O,N)3 ± δ was orthorhombic Pnma due to the tilt and rotation of the anion octahedra, compared to cubic Pm3¯m of EuTiO3 (at room temperature). The thermoelectric properties of oxynitride polycrystalline bodies sintered in three different ways were investigated in the temperature range of 300 K < T < 950 K. The Seebeck coefficients (S) of the oxynitrides were lower compared with the oxide, and the electrical resistivities (ρ) were increased about one order of magnitude. The activation energies (E A) indicated a larger band gap of EuTi(O,N)3 ± δ when compared to the pristine EuTiO3 (∼1.3 eV compared to 0.98 eV). A morphological characterization by transmission electron microscopy and scanning electron microscopy illustrated intrinsic nanopores within the individual particles and weak grain-interconnections indicating poor intergrain electron transport. Ab initio calculations of the electronic structures confirmed a larger band gap of the distorted crystal structure of the oxynitride and showed a decrease of the density of states at the Fermi level, explaining the reduction of the measured S.