Investigation of the Impact of Transient Heat Loads Applied by Laser Irradiation on ITER-Grade Tungsten

Huber, Alexander; Steudel, Isabel; Mertens, Philippe; Zlobinski, M.; Arakcheev, A.; Sergienko, Gennady; Unterberg, Bernhard; Kreter, Arkadi; Burdakov, A. V.; Samm, Ulrich; Linke, Jochen; Shoshin, A.; Coenen, Jan Willem; Wirtz, Marius; Pintsuk, Gerald; Philipps, V.; Schweer, Bernd; Reinhart, Michael

doi:10.1088/0031-8949/2014/T159/014005

Journal Article

FZJ-2014-03804

Investigation of the Impact of Transient Heat Loads Applied by Laser Irradiation on ITER-Grade Tungsten

Huber, A. (Corresponding Author)FZJ* ; Arakcheev, A. ; Sergienko, G.FZJ* ; Steudel, I.FZJ* ; Wirtz, M.FZJ* ; Burdakov, A. V. ; Coenen, J. W.FZJ* ; Kreter, A.FZJ* ; Linke, J.FZJ* ; Mertens, P.FZJ* ; Philipps, V.FZJ* ; Pintsuk, G.FZJ* ; Reinhart, M.FZJ* ; Samm, U.FZJ* ; Shoshin, A. ; Schweer, B.FZJ* ; Unterberg, B.FZJ* ; Zlobinski, M.

2014
IoP Publ. Bristol

Physica scripta T159, 014005 (2014) [10.1088/0031-8949/2014/T159/014005]

This record in other databases:

Please use a persistent id in citations: http://hdl.handle.net/2128/7833 doi:10.1088/0031-8949/2014/T159/014005

Abstract: Cracking thresholds and crack patterns in tungsten targets after repetitive ITER-like edge localized mode (ELM) pulses have been studied in recent simulation experiments by laser irradiation. The tungsten specimens were tested under selected conditions to quantify the thermal shock response. A Nd:YAG laser capable of delivering up to 32 J of energy per pulse with a duration of 1 ms at the fundamental wavelength λ = 1064 nm has been used to irradiate ITER-grade tungsten samples with repetitive heat loads. The laser exposures were performed for targets at room temperature (RT) as well as for targets preheated to 400 °C to measure the effects of the ELM-like loading conditions on the formation and development of cracks. The magnitude of the heat loads was 0.19, 0.38, 0.76 and 0.90 MJ m−2 (below the melting threshold) with a pulse duration of 1 ms. The tungsten surface was analysed after 100 and 1000 laser pulses to investigate the influence of material modification by plasma exposures on the cracking threshold. The observed damage threshold for ITER-grade W lies between 0.38 and 0.76 GW m−2. Continued cycling up to 1000 pulses at RT results in enhanced erosion of crack edges and crack edge melting. At the base temperature of 400 °C, the formation of cracks is suppressed.