| Home > Publications database > Electrochemical Performance and Degradation Analysis of an SOFC Short Stack Following Operation of More than 100,000 Hours |
| Home > Publications database > Electrochemical Performance and Degradation Analysis of an SOFC Short Stack Following Operation of More than 100,000 Hours |
| Journal Article | FZJ-2020-01177 |
; ;
2019
Electrochemical Soc.
Pennington, NJ
This record in other databases: 
Please use a persistent id in citations: http://hdl.handle.net/2128/24385 doi:10.1149/2.0751916jes
Abstract: From August 2007 to January 2019, a two-layer solid oxide fuel cell (SOFC) short stack of a planer design with zirconia-based, anode-supported cells (ASC) and ITM interconnectors (with 26% chromium content) was tested with hydrogen and compressed air at a furnace temperature of 700°C for more than 100,000 hours, of which ~93,000 were in constant current mode, with a current density of 0.5 Acm−2 and with a fuel utilization of 40%. The calculated voltage degradation rate slowly decreased, from ~8.0 mV/kh (~1.0%/kh) for the first 40,000 h to ~1.4 mV/kh (~0.2%/kh) for the subsequent operation under load, indicating different dominating degradation mechanisms. The average voltage and area-specific resistance (ASR) degradation rates for the complete operating period under electrical load were 0.5%/kh and 2.5%/kh, respectively. Electrochemical impedance spectroscopy (EIS) was also implemented at the end of the testing period for the purpose of electrochemical characterization and a degradation analysis. The post-mortem analysis of the stack is currently in preparation. In this study, the performance and degradation behavior of the stack and cells are analyzed and discussed on the basis of the electrochemical measurements collected.
; 
; 
; Clarivate Analytics Master Journal List ; Current Contents - Engineering, Computing and Technology ; Current Contents - Physical, Chemical and Earth Sciences ; IF < 5 ; JCR ; SCOPUS ; Science Citation Index ; Science Citation Index Expanded ; Web of Science Core Collection
|
The record appears in these collections: |
PDF
PDF (PDFA)