http://join2-wiki.gsi.de/foswiki/pub/Main/Artwork/join2_logo100x88.png Effect of thermal insulation on microstructural homogeneity and onset temperature of flash sintered materials

Storion, A. G. (Corresponding author) ; Lavagnini, I. R. ; Campos, J. V. ; da Silva, J. G. P.FZJ* ; Maestrelli, S. C. ; Pallone, E. M. J. A.

2021
Elsevier Science Amsterdam [u.a.]

This record in other databases:  

Please use a persistent id in citations: http://hdl.handle.net/2128/30942  doi:10.1016/j.jeurceramsoc.2021.08.060

Abstract: The present work aimed to reduce the microstructure heterogeneity inherent to flash sintering by using alumina blankets as a thermal insulator around ZnO cylindrical samples during the sintering process, under different electric field conditions. Thermal insulation significantly reduced the flash onset temperature and the grain size heterogeneity. For higher electric fields, a temperature reduction as high as 480 °C was observed, which also led to lower densification. These findings were discussed in terms of changes in the heat loss dynamics coupled with the adsorbed water retention, both promoted by the applied thermal insulation. A model to estimate the temperature at stage III of flash sintering was proposed. The final temperature reached with thermal insulation did not differ significantly from the ones without it. Thus, thermal insulation could represent an alternative route to flash sinter materials with lower furnace temperatures with energy savings up to 78 % and a more homogeneous microstructure.

---

Contributing Institute(s):

1. Werkstoffsynthese und Herstellungsverfahren (IEK-1)

Research Program(s):

1. 899 - ohne Topic (POF4-899) (POF4-899)

Appears in the scientific report 2022

---

Database coverage:
; ; ; Clarivate Analytics Master Journal List ; Current Contents - Engineering, Computing and Technology ; Current Contents - Physical, Chemical and Earth Sciences ; Ebsco Academic Search ; Essential Science Indicators ; IF < 5 ; JCR ; SCOPUS ; Science Citation Index Expanded ; Web of Science Core Collection

---