http://join2-wiki.gsi.de/foswiki/pub/Main/Artwork/join2_logo100x88.png Study of Ni–Cr / CrN bilayer thin films resistor prepared by magnetron sputtering

Lee, Y.-C. (Corresponding author) ; Yen, V. C. ; Pithan, C.FZJ* ; Jan, J.-H.

2023
Elsevier Science Amsterdam [u.a.]

This record in other databases:  

Please use a persistent id in citations: doi:10.1016/j.vacuum.2023.112085  doi:10.34734/FZJ-2023-01841

Abstract: In this study, we prepare bilayer Ni–Cr/CrN films. A Ni–Cr resistive thin film was prepared by DC sputtering from targets of Ni0.8-Cr0.2 casting alloy. A CrN protection thin film was prepared based on optimum sputtering conditions of the Ni–Cr film, which was made by DC and RF magnetron co-sputtering from targets of Ni0.8-Cr0.2 casting alloy and chromium. The electrical properties and microstructures of the resistive films at different annealing temperatures were investigated. The phase evolution, microstructural and composition of Ni–Cr and NiCr/CrN films were characterized by X-ray diffraction (XRD), field-emission transmission electron microscopy (HRTEM) and auger electron spectroscopy (AES). The results indicated that the resistivity of the bilayer Ni–Cr/CrN films is higher than Ni–Cr films. When the annealing temperature was set to 300 °C, the bilayer Ni–Cr/CrN films exhibited a resistivity ∼303 μΩ cm with the smallest temperature coefficient of resistance (TCR) of −3 ppm/°C. However, the Ni–Cr films that annealed at 300 °C showed a resistivity of ∼210 μΩ cm, with a TCR of 13 ppm/°C. In addition, the TCR and resistivity variation rate of CrN protective coating layer on the Ni–Cr films after high temperature testing at 150 °C up to 100 h was done. The results show that the average change rate of the TCR for bilayer Ni–Cr/CrN films is lower than single Ni–Cr films.

---

Contributing Institute(s):

1. Elektronische Materialien (PGI-7)
2. JARA-FIT (JARA-FIT)

Research Program(s):

1. 5233 - Memristive Materials and Devices (POF4-523) (POF4-523)

Appears in the scientific report 2023

---

Database coverage:
; ; Clarivate Analytics Master Journal List ; Current Contents - Engineering, Computing and Technology ; Current Contents - Physical, Chemical and Earth Sciences ; Ebsco Academic Search ; Essential Science Indicators ; IF < 5 ; JCR ; Nationallizenz ; SCOPUS ; Science Citation Index Expanded ; Web of Science Core Collection

---