| Home > Publications database > Post-test characterization of a solid oxide fuel cell stack operated for more than 30,000 hours: The cell |
| Home > Publications database > Post-test characterization of a solid oxide fuel cell stack operated for more than 30,000 hours: The cell |
| Journal Article | FZJ-2017-07540 |
; ;
2018
Elsevier
New York, NY [u.a.]
This record in other databases: 
Please use a persistent id in citations: doi:10.1016/j.jpowsour.2017.11.025
Abstract: A four-layer solid oxide fuel cell stack with planar anode-supported cells was operated galvanostatically at 700 °C and 0.5Acm−2 for nearly 35,000 h. One of the four planes started to degrade more rapidly after ∼28,000 h and finally more progressively after ∼33,000 h. The stack was then shut down and a post-test analysis was carefully performed. The cell was characterized with respect to cathodic impurities and clarification of the reason(s) for failure. Wet chemical analysis revealed very low chromium incorporation into the cathode. However, SEM and TEM observations on polished and fractured surfaces showed catastrophic failure in the degraded layer. The cathode–barrier–electrolyte cell layer system delaminated from the entire cell over large areas. The source of delamination was the formation of a porous, sponge-like secondary phase consisting of zirconia, yttria and manganese (oxide). Large secondary phase islands grew from the electrolyte–anode interface towards the anode and cracked the bonding between both layers. The manganese originated from the contact or protection layers used on the air side. This stack result shows that volatile species – in this case manganese – should be avoided, especially when long-term applications are envisaged.
; Current Contents - Engineering, Computing and Technology ; Current Contents - Physical, Chemical and Earth Sciences ; Ebsco Academic Search ; IF >= 5 ; JCR ; NCBI Molecular Biology Database ; SCOPUS ; Science Citation Index ; Science Citation Index Expanded ; Thomson Reuters Master Journal List ; Web of Science Core Collection
|
The record appears in these collections: |
PDF
PDF (PDFA)