| Hauptseite > Publikationsdatenbank > Current channeling along extended defects during electroreduction of SrTiO3 |
| Hauptseite > Publikationsdatenbank > Current channeling along extended defects during electroreduction of SrTiO3 |
| Journal Article | FZJ-2019-01748 |
; ; ; ; ; ;
2019
Macmillan Publishers Limited, part of Springer Nature
[London]
This record in other databases: 
Please use a persistent id in citations: http://hdl.handle.net/2128/21786 doi:10.1038/s41598-019-39372-2
Abstract: Electroreduction experiments on metal oxides are well established for investigating the nature of the material change in memresistive devices, whose basic working principle is an electrically-induced reduction. While numerous research studies on this topic have been conducted, the influence of extended defects such as dislocations has not been addressed in detail hitherto. Here, we show by employing thermal microscopy to detect local Joule heating effects in the first stage of electroreduction of SrTiO3 that the current is channelled along extended defects such as dislocations which were introduced mechanically by scratching or sawing. After prolonged degradation, the matrix of the crystal is also electroreduced and the influence of the initially present dislocations diminished. At this stage, a hotspot at the anode develops due to stoichiometry polarisation leading not only to the gliding of existing dislocations, but also to the evolution of new dislocations. Such a formation is caused by electrical and thermal stress showing dislocations may play a significant role in resistive switching effects.
; 
; 
; 
; BIOSIS Previews ; Clarivate Analytics Master Journal List ; Current Contents - Physical, Chemical and Earth Sciences ; DOAJ Seal ; Ebsco Academic Search ; IF < 5 ; JCR ; NCBI Molecular Biology Database ; PubMed Central ; SCOPUS ; Science Citation Index ; Science Citation Index Expanded ; Web of Science Core Collection ; Zoological Record
|
The record appears in these collections: |
PDF
PDF (PDFA)